Заказать металлопрокат - Металлсервис

Заказать металлопрокат - Металлсервис
Заказать металлопрокат, листовой прокат, трубный прокат, сортовой прокат, метизная продукция - Металлсервис Уральск, Актау, Актобе

Our Branches

Uralsk

246/11 Evrazia Avenue, Uralsk, Kazakhstan, 090001

Phone\fax:

+ 7 (7112) 544-000, 543-000
+ 7 (7112) 237-503, 237-817
+ 7 (701) 767-29-84

Email:

galkin@metall-service.kzinfo@metall-service.kz

Work schedule:

Mon-Fri: 09.00-18.00h
Break from 13.00 to 14.00h

Saturday - Sunday: 09.00-13.00h

Aktobe

185B Zinchenko str, 41 siding, Aktobe

Phone\fax:

+ 7 (7132) 407-407, 407-382
+ 7 (701) 968-89-36

Email:

irina@metall-service.kz
artur@metall-service.kz

Work schedule:

Mon-Fri: 09.00-18.00
Break from 13.00 to 14.00

Saturday - Sunday: 09.00-13.00

Aktau

"Recon-Aktau" base, Industrial Zone, Aktau

Phone\fax:

+ 7 (7292) 544-445, 544-592, 550-050
+ 7 (701) 767-31-39

Email:

nikolai@metall-service.kz

Work schedule:

Mon-Fri: 09.00-18.00
Break from 13.00 to 14.00

Saturday - Sunday: 09.00-13.00

Atyrau

33 Building, South Industrial Area, Atyrau, Kazakhstan, 060000

Phone/fax:

+7 (7122) 76-33-00
+7 (7122) 76-33-76
+7 (7122) 76-36-26
+7 (7122) 76-36-96

Mob:

+7 (701) 027-28-59

Email:

kurdov@metall-service.kz sasha@metall-service.kz

Work schedule:

Mon-Fri: 09.00-18.00h
Break from 13.00 to 14.00h

Saturday - Sunday 09.00 – 13.00h

Kostanay

2/1 Karbishev str base Mansion Kostanay Kazakhstan 110000

Phone/fax:

+7 (7142) 39-40-80
+7 (7142) 39-40-88

Mob:

+7 (701) 029 08 37

Email:

galkin@metall-service.kz

Work schedule:

Mon-Fri: 09.00-18.00h
Break from 13.00 to 14.00h

Saturday - Sunday 09.00 – 13.00h

Kyzylorda

20 Hong Bin Do str.

Phone/fax:

+ 7 (7242) 259-111, 259-559, 259-577
+7 (701) 034-64-50

Email:

aset@metall-service.kz

Work shedule:

Mon-Fri: 09.00-18.00h
Break from 13.00 to 14.00h

Saturday - Sunday 09.00–13.00h

Company Handbook of metal-roll Examples of function of the steel grades

Examples of function of the steel grades

Using of carbon high-grade structural steel

08кп, 10

Elements , manufacturihg by cold stamping and cold - heading , pipes , gaskets , fasteners , caps . Carbonized and cyanized components, not requiring high-tensile core (bushes, rollers, buffer stops, templets, gears, friction disks)

15, 20

Light loaded elements (rollers, пальцы, buffer stops, templets, axles, gears). Thin galling elements, levers, hooks, transverse beams, insertion pieces, bolts, drawbars etc.

30, 35

Elements, undergoing low tension (shafts, spindles, sprockets, drawbars, transverse beams, levers, disks, shafting)

40, 45

Elements with increasing durability (crankshafts, connecting rods, gear rims, camshafts, flywheels, gears, studs, ratchets, plungers, spindle shafts, friction disks, axles, clutches, racks, rolls etc.)

50, 55

Gears, rolls, guide bars, binding bands, shafts, eccentrics, light loaded springs and shocks etc. Used after quenching with high-temperature tempering and in normalized condition.

60

Elements with high strength and spring characteristics (rolls, eccentrics, spindles, spring rings, springs and clutch plates, shock springs). Used after quenching or normalizing (heavy members)

Using of low alloy sheet steel and broadband universal steel

09Г2

For elements of welded constructions made from sheet steel. Satisfactorily cutting.

09Г2С

For steam boilers, devices and tanks pressure-operated at -70 - +450 °С; for steel-plate welded constructions in chemical and oil engineering, shipbuilding. Well welding. Satisfactorily cutting.

10ХСНД

For welded constructions in chemical engineering, shipbuilding shaped sections, carriage engineering.

15ХСНД

For elements of carriages, poling, shipbuilding intricate profiles. Raised corrosion resistance

15ГФ

For steel-plate welded constructions in carriage engineering. Provides high grade of weld seam. Satisfactorily stamping.

Using of alloy structural steel

15Х

Piston pins, cam shafts, push bars, trunnion crosses, valves, small parts, frictional wear bearing. Well cement stabilization.

20Х

Cam clutchs, bushs, spindles, sliding bars, plungers, driftpins, templet toolings, spline rolls etc.

40Х

For elements functioning at average speed and average pressure (gears, spindles and shaft in frictionless bearings, worm shafts)

45Х, 50Х

For heavy elements functioning at average speed of low pressure (gears, spindles, shafts in frictionless bearings, worm and spline shafting). High tensile strength and and viscosity

38ХА

For gears, functioning at average speed and average pressure.

45Г2, 50Г2

For heavy low-loaded elements (spindels, shafts, gears of heavy machines).

18ХГТ

For elements functioning at fair speed and high-pressure and load impact (gears, spindels, claw clutchs, hubs etc.)

20ХГР

For heavyloaded elements, functioning at fair speed and load impact

15ХФ

For medium-sized elements, cemented and hardened with low-temperature tempering (gears, gudgeon pins etc.)

40ХС

For fine elements of high tensile strength

40ХФА

For high-strength elements hardened and high-temperature tempered; for wear odd-shaped average and small elements, functioning (levers, tappets); for strength welded constructions, functioning at alternating load.

35ХМ

For shafts, elements of turbines and fasteners, functioning at higher temperature.

45ХН, 50ХН

Similarly to use of steel grade 40Х, for heavy elements.

Using of corrosionproof steel and alloy combinations

20Х13, 08Х13, 12Х13, 25Х13Н2

For elements with raised ductility, load impacted; elements, functioning at mild environment.

30Х13, 40Х13, 08Х18Т1

For hard elements; cutting, measuring, surgical instruments, valve plates of compressors etc. (sttteel 08Х18Т1 hase best Olsen ductility)

06ХН28МТ

For welded construction, functioning at middle corrosive medium (hot phosphoric acid, sulphuric acid up to 10% etc.)

14X17H2

For various elements of chemical and aircraft industry. Possessing high technological properties.

95Х18

For elements of high body hardness, functioning at wear conditions.

08X17T

Recommended as substitute of steel 12Х18Н10Т for constructions unshocked at operation temperature to - 20 °С

15X25T, 15Х28

Similarly to steel grade 08X17T, for elements, functioning at more hostile environment af temperature – from 20 up to 400 °С (15Х28 - for glass jointing)

20Х13Н4Г9, 10Х14АГ15, 10Х14Г14НЗ

Steel substitute 12X18H9, 17Х18Н9 for welded constructions.

09Х15Н8Ю, 07X16H6

For high-strength products, springing elements; steel grade 09Х15Н8Ю - for acetic and saline agents.

08X17H5M3

For elements functioning at sulphate.

20X17H2

For high-strength heavy loaded elements functioning at fretting and shocking in low aggressive environment.

10Х14Г14Н4Т

Steel substitute 12Х18Н10Т for elements, functioning at low aggressive environment, and up to 196 °С

12Х17Г9АН4, 15Х17АГ14 03Х16Н15МЗБ, 03X16H15M3

For elements functioning at atmospheric conditions (steel substitute 12X18H9,12Х18Н10Т). For welded constructions functioning at boiling phosphoric, sulphuric and 10 % acetic acid.

15Х18Н12С4ТЮ

For welded constructions functioning at aerial and hostile environment ang aquafortis.

08X10H20T2

Nonmagnetic steel for elements functioning at salt water.

04X18H10, 03X18H11, 03X18H12, 08X18H10, 12X18H9, 12X18H12T, 08X18H12T, 06X18H11

For elements functioning at nitric acid at high-temperature

12Х18Н10Т, 12Х18Н9Т, 06ХН28МДТ, 03ХН28МДТ

For welded constructions in various industrial sectors. For welded constructions functioning at up to 80 °С in sulphuric acid of various concentrations (not recommended 55 % acetic and phosphoric acid)

09Х16Н4Б

For high-strength stamped and welded constructions and elements functioning at contact with hostile environment.

07Х21Г7АН5

For welded constructions functioning at up to + 253 °С and in middle hostile environment.

03Х21Н21М4ГБ

For welded constructions functioning at hot phosphoric and low concentrated sulfuric acid up to 80 °С, nitric acid при up to 95°С

ХН65МВ

For welded constructions functioning at high temperature in sulfuric and hydrochloric solutions and in acetic acid.

Н70МФ

For welded constructions functioning at high temperature in hydrochloric, sulfuric, phosphoric acid and the other environment of reduction.

Using of tool plain steel of various grades

У7, У7А

For harvesting: axes, cleavers, chisels, chippers. For small air tools: chisels, swages, strikers. For blacksmith's stamps. For needle wire. For machinist's tools: hammers, beetles, drifts, screwdrivers, compound pliers, nippers, oblique cutting pliers etc.

У8, У8А, У8Г, У8ГА, У9, У9А

For tools functioning at conditions without heating of cutting edge. For harvesting: cutters, reamers, forgings, axes, chisels, chippers, crown and circular saws. For crimping wheels, plates and rods for mold injection casting of tin and lead metals. For locksmith's and insertion tools: rivet sets, centre punches, drifts, screwdrivers, compound pliers, nippers, oblique cutting pliers. For templets of simple form and reduced quality grade. For cold-rolled metal strip with thickness from 2,5 to 0,02 mm, for manufacturing of flat and wrap springs and spring odd-shaped elements, valves, dipsticks, reeds, lamels of splitting knives, small constructional elements, for timers etc.

У10А, У12А

For cores.

У10, У10А

For needle wire.

У10, У10А, У11, У11А

For tools functioning at conditions of cutting edge unheating. For harvesting: crown handsaws and bucksaws, frame saws, augers. For small cold-pressing dies (cupping, heading , trimming and punching dies) without abrupt junction in section. For simple form fixed gages and reduced grades of accuracy. For dies, files, scraping tools etc. For cold-rolled strip of thickness from 2,5 up to 0,02 mm, for manufacturing of flat and wound springs and odd-shaped spring elements, valves, dipsticks, reeds, lamels of splitting knives, small constructional elements, for timers etc.

У12, У12А

For hand taps, files, scraping tools. Small cold-stamping, trimming and punching dies without abrupt junction in section, cold-upsetting drifters and stamps, simple form templets and reduced quality grades.

У13, У13А

Fortools with reduced wearability for medium and significant specific pressure (without heating of cutting edge); files, shaving blades and knives, sharp surgical instruments, scraping tools, etching devices.

Using of spring steel

60С2, 60С2А

For carriage springs from strip steel of thickness 3 - 16 mm and spring strip steel of thickness 0,08 - 3 mm; for wound spring from steel wire with diameter 3 - 16 mm. Bad cutting. Peak operation temperature 250 °С

70СЗА

For heavy loaded high-duty springs. Addiction to graphitic corrosion.

50ХГ, 50ХГА

For carriage springs from strip steel of thickness 3 - 18 mm. Bad cutting.

50ХФА, 50ХГФА

For high-duty carriage springs functioning at higher temperature (up to 300 °С); for springs subjected by multiple varying load.

60C2XA

For large heavy loaded high-duty carriage springs.

60C2H2A, 65C2BA

For heavy loaded high-duty carriage springs from gage steel and spring strips.

Using of electrotechnical sheet steel

1211,1212, 1213, 22110

For armatures and electric poles of dc electric machines for rotors and stators of asynchronous motors of industrial-frequency power up to 100 kilowatt for instruments. High ductility.

1311, 1312

For rotors and stators of asynchronous motors of power from 100 to 400 kilowatt. Good ductility.

1411,1412, 2411

For rotors and stators of asynchronous motors of power 400 - 1000 kilowatt, small-power transformers for oversampling motors. Satisfactory ductility.